 = Qs of system = ## page was renamed from CLIO/Technicals/Qofpendulum
## page was renamed from CLIO/req/Qofpendulum
= Qs of system =
Line 20: Line 22:
    * 300K: 10^7^　(ただし、室温かつ観測帯域ではthermoelastic dampingが支配的。)     * 300K: 10^7^　(ただし、室温かつ観測帯域ではthermoelastic dampingによる熱雑音が支配的。)

Qs of system

  • 熱雑音の計算に使用している値をリスト
  • Suspension
    • Bolfure

      • 300K: 103 (みよきさんの測定あり)

      • Cryogenic: 104

    • Copper-Beryllium(Anneled)(板バネに使用。バルク材について低温測定の文献あり。今、手元に無し。)

      • 300K: 104

      • Cryogenic: 105

    • Pure Al wire (笠原測定あり。ヒートリンク、最終段ワイヤーに使用。)

      • 300K: 103

      • Cryogenic: 104

    • Sapphire fiber(内山測定あり)

      • 300K: 4*103 (thermoelastic effect. 直径に依存。値は直径250ミクロン、100Hzで計算。)

      • Cryogenic: 106 (測定では10Kで、5*106 - 1*107が得られている。)

  • Mirror
    • Structure of sapphire（内山測定あり）

      • 300K: 107　(ただし、室温かつ観測帯域ではthermoelastic dampingによる熱雑音が支配的。)

      • 20K: 108

    • Structure of coating (dissipation, 山元測定あり)

      • 300K - Cryogenic: 4*10-4