== Suspect on mirror optical losses by H.Yamamoto == |
| Line 8: | Line 3: |
| . 私としては不可能と信じていますが、一応どの様な表面が必要か。 散乱によるロスは * 鏡の長波長(>1 mm) RMS = 1 nm で鏡あたりの散乱損失が 45ppm. '''0.75 nm で 25ppm''' * 鏡の短波長(<1 mm) RMS = 0.2 nm で '''6ppm''' * 訳の分からない点状散乱 '''10ppm''' （神様、仏様に祈ってやっと願いがかなうかどうか、15~30ppm が現実的な値） . この散乱だけで 61ppm (RMS(長波長)=1nm), '''41ppm (RMS=0.75nm)''' |
* Scattering loss of 45ppm by low-freq (>1mm) surface error of 1nm RMS (25ppm with 0.75nm RMS). * Scattering loss of 6ppm by high-freq (<1mm) surface error of 0.2nm RMS. * Unexplainable punctate scattering loss of 10ppm (realistic estimate would be 15-30ppm). |
| Line 14: | Line 7: |
| These alone would make the total scattering loss already 61ppm (with 1nm LF RMS) or 41ppm (with 0.75nm LF RMS). | |
| Line 15: | Line 9: |
| . シリカの場合、コーティングによる吸収が 0.5ppm 以下が可能と言われているが、表面が汚れると数 ppm 簡単に悪くなる。 . この中で、金と時間で解決できるのが長波長領域での散乱ロス。 LIGO は RMS＜0.5 nm を要求し、 Tinsley がそれより良い研磨を達成している。 |
* Besides, absorption at the coatings, assumed to be 0.5ppm, can go worse by a few ppm easily. * LF RMS could be improved if we spend a lot of money and time. LIGO asked for RMS<0.5nm and Tinsley. |
Suspect on mirror optical losses by H.Yamamoto
Scattering loss of 45ppm by low-freq (>1mm) surface error of 1nm RMS (25ppm with 0.75nm RMS).
Scattering loss of 6ppm by high-freq (<1mm) surface error of 0.2nm RMS.
- Unexplainable punctate scattering loss of 10ppm (realistic estimate would be 15-30ppm).
These alone would make the total scattering loss already 61ppm (with 1nm LF RMS) or 41ppm (with 0.75nm LF RMS).
- Besides, absorption at the coatings, assumed to be 0.5ppm, can go worse by a few ppm easily.
LF RMS could be improved if we spend a lot of money and time. LIGO asked for RMS<0.5nm and Tinsley.