2692
Comment:
|
2689
|
Deletions are marked like this. | Additions are marked like this. |
Line 15: | Line 15: |
|| Temperature of suspension || 20K || || | || Bulk absorption || 20ppm/cm || [[LCGT/subgroup/ifo/ISC/TaskList/CurrentStatus/ClassicalNoise/issue4|issue 4]] || || Coating absorption || 0.1ppm/cm || [[LCGT/subgroup/ifo/ISC/TaskList/CurrentStatus/ClassicalNoise/issue4|issue 4]] || || Temperature of mirrors || 20K || || |
Line 19: | Line 21: |
|| Mechanical loss of Silica coating || 1e-4 ||[[LCGT/subgroup/ifo/ISC/TaskList/CurrentStatus/ClassicalNoise/issue5|issue 4]]|| || Mechanical loss of Tantala coating || 4e-4 ||[[LCGT/subgroup/ifo/ISC/TaskList/CurrentStatus/ClassicalNoise/issue5|issue 4]]|| || Optical loss of each arm || 70ppm/roundtrip ||[[LCGT/subgroup/ifo/ISC/TaskList/CurrentStatus/ClassicalNoise/issue6|issue 5]]|| |
|| Mechanical loss of Silica coating || 1e-4 ||[[LCGT/subgroup/ifo/ISC/TaskList/CurrentStatus/ClassicalNoise/issue5|issue 5]]|| || Mechanical loss of Tantala coating || 4e-4 ||[[LCGT/subgroup/ifo/ISC/TaskList/CurrentStatus/ClassicalNoise/issue5|issue 5]]|| || Optical loss of each arm || 70ppm/roundtrip ||[[LCGT/subgroup/ifo/ISC/TaskList/CurrentStatus/ClassicalNoise/issue6|issue 6]]|| |
Line 24: | Line 26: |
|| Bulk absorption || 20ppm/cm || [[LCGT/subgroup/ifo/ISC/TaskList/CurrentStatus/ClassicalNoise/issue4|issue 6]] || || Coating absorption || 0.1ppm/cm || [[LCGT/subgroup/ifo/ISC/TaskList/CurrentStatus/ClassicalNoise/issue4|issue 6]] || |
Classical-Noise parameters
There are some issues to be discussed.
Beam radius |
3cm |
|
Suspension length |
40cm |
|
Suspension thickness |
1.8mm |
|
Number of suspension fiber |
4 |
|
Temperature of suspension |
16K |
|
Mechanical loss of fiber |
2e-7 |
|
Mirror radius |
12.5cm |
|
Mirror thickness |
15cm |
|
Bulk absorption |
20ppm/cm |
|
Coating absorption |
0.1ppm/cm |
|
Temperature of mirrors |
20K |
|
Mechanical loss of mirror |
1e-8 |
|
Number of coatings (ITM) |
9 |
|
Number of coatings (ETM) |
18 |
|
Mechanical loss of Silica coating |
1e-4 |
|
Mechanical loss of Tantala coating |
4e-4 |
|
Optical loss of each arm |
70ppm/roundtrip |
|
Optical loss in the SRC |
2% |
|
Optical loss at the PD |
10% |
|
Physical constants
Young's modulus of Sapphire |
4e11 Pa |
Density of Sapphire |
4e3 kg/m^3 |
Poisson ratio of Sapphire |
0.29 |
Thermal expansion of Sapphire (20K) |
5.6e-9 /K |
Specific heat of Sapphire (20K) |
0.69 J/K/kg |
Thermal conductivity of Sapphire (20K) |
1.57e4 W/m |
Thermal expansion of Sapphire (300K) |
5.0e-6 /K |
Specific heat of Sapphire (300K) |
790 J/K |
Thermal conductivity of Sapphire (300K) |
40 W/m/K |
Young's modulus of Silica |
7.2e10 Pa |
Poisson ratio of Silica |
0.17 |
Refraction index of Silica |
1.45 |
Thermal expansion of Silica (300K) |
5.1e-7 /K |
Specific heat per volume of Silica (300K) |
1.64e6 J/K/m^3 |
Thermal conductivity of Silica (300K) |
1.38 W/m |
dn/dT of Silica (300K) |
8e-6 /K |
Young's modulus of Tantala |
1.4e11 Pa |
Poisson ratio of Tantala |
0.23 |
Refraction index of Tantala |
2.07 |
Thermal expansion of Tantala (300K) |
3.6e-7 /K |
Specific heat per volume of Tantala (300K) |
2.1e6 J/K/m^3 |
Thermal conductivity of Tantala (300K) |
33 W/m/K |
dn/dT of Tantala (300K) |
14e-6 /K |